MONEL R-405

没有此类产品
产品描述
The free-machining version of MONEL alloy 400.
A controlled amount of sulfur is added to the
alloy to provide sulfide inclusions that act as chip
breakers during machining. Other characteristics
are essentially the same as those of MONEL alloy
400. Used for meter and valve parts, fasteners
and screw-machine products.
STANDARD PRODUCT FORMS
Round bar, hexagon and wire.
MAJOR SPECIFICATIONS
UNS N04405
NACE MR-01-75
ASTM B 164
ASME SB-164
SAE AMS 4674, 7234
QQ-N 281
MIL-N-894
LIMITING CHEMICAL COMPOSITION, %
Nia.........63.0 min.
Cu.....28.0 – 34.0
Fe........... 2.5 max.
aPlus Co.
S.... 0.025 – 0.060
Mn.......... 2.0 max.
C............. 0.3 max.
Si............ 0.5 max.
PHYSICAL CONSTANTS AND THERMAL PROPERTIES
Density, Ib/in3..........................................................................0.318
g/cm3......................................................................... 8.80
Melting Point, °F......................................................2370 – 2460
°C......................................................1300 – 1350
Specific Heat, Btu/lb •°F.....................................................0.102
J/kg •°C........................................................... 427
Curie Temperature, °F....................................................70 – 120
°C.....................................................20 – 50
Coefficient of Expansion, 70 – 200°F, 10-6 in/in •°F........ 7.6
20 – 95°C, μm/m •°C............. 13.7
Thermal Conductivity, Btu • in/ft2• h•°F............................ 151
W/m•°C........................................... 21.8
Electrical Resistivity, ohm • circ mil/ft.............................. 307
μΩ•m...............................................0.510
TYPICAL MECHANICAL PROPERTIES
MONEL  R-405
Corresponding parameter set not found, please add it in property template of background
暂未实现,敬请期待
暂未实现,敬请期待